OmniPro™ CPP 10M FR0
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniPro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | huCN9t_OmniPro-CPP-10M-FR0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame Resistant, Copolymer Polypropylene |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.988 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 24.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 100 | % | ASTM D638 |
| Flexural Modulus | 1170 | MPa | ASTM D790 |
| Flexural Strength | 33.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.18 mm) | 85.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | V-0 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 193 to 238 | °C | |
| Middle Temperature | 193 to 238 | °C | |
| Front Temperature | 193 to 238 | °C | |
| Nozzle Temperature | 193 to 238 | °C | |
| Processing (Melt) Temp | 193 to 238 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene CPP1030 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| NANCAR® 1204D | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| NYLAFORCE® dynamic A 60 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | NYLAFORCE® dynamic |
| Cellophane™ K195HB20/23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Dryflex® 502850S | ELASTO | SEBS | Dryflex® |