TEKALOY™ G70NHT
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | huAZGS_TEKALOY-G70NHT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| G70NHT is a PC/ABS alloy. G70NHT has good properties with high flow, impact resistance, flame retardant and good processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 58.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 55 | % | ASTM D638 |
| Flexural Modulus 3 | 2450 | MPa | ASTM D790 |
| Flexural Strength 4 | 93.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 440 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 104 | °C | |
| 1.8 MPa, Unannealed | 95.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 230 to 270 | °C | |
| Middle Temperature | 230 to 270 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Nozzle Temperature | 240 to 280 | °C | |
| Processing (Melt) Temp | 240 to 280 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BUM 30 | Arkema | Nylon 11 | Rilsan® |
| Talcoprene® 1030TC BIANCO280 | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Anjacom® R050/65S | Almaak International GmbH | PC+ABS | Anjacom® |
| Hifax X M1 T11 | LyondellBasell Industries | PP Alloy | Hifax |
| INLUBE POMHSI2 | Infinity LTL Engineered Compounds | Acetal (POM) Homopolymer | INLUBE |