Order Products : sales@su-jiao.com
RAMSHINE PV1003
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMSHINE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hsvR1h_RAMSHINE-PV1003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GENERAL PURPOSE ABS FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 30 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| -- | 0.40 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.30 | % | ASTM D570 |
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 119 | ASTM D785 | |
| R scale | 119 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 34.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 20 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D256 |
| 23°C | 22 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 84.0 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 98.0 | °C | ASTM D1525, ISO 306 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 205 - 220 | °C | |
| Front Temperature | 220 - 250 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 35.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PROTEQ™ C18UST5L | Marplex Australia Pty. Ltd. | PP Copolymer | PROTEQ™ |
| SLOVASTER® B1 GF 10 FRX 5 | Plastcom | PBT | SLOVASTER® |
| ALTECH® PP-H A 1000/620 UV | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| Hifax TRC 221P 3 | LyondellBasell Industries | PP Copolymer | Hifax |
| Huaxia Shenzhou FKM 246D | Shandong Huaxia Shenzhou New Material Co., Ltd. | Fluorelastomer | Huaxia Shenzhou |