LNP™ LUBRICOMP™ RFN14 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hsoVa4_LNP-LUBRICOMP-RFN14-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFN14 is a compound based on Nylon 66 containing 20% Glass Fiber, 5% MOS2. Added features of this grade include: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound RFL-4214 Product reorder name: RFN14 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.33 | g/cm³ | |
| -- | 1.32 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.60 | % | |
| Across Flow : 24 hr | 0.80 to 2.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.67 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.96 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8860 | MPa | ASTM D638 |
| -- | 8530 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 135 | MPa | ASTM D638 |
| Break | 134 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.9 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 7450 | MPa | ASTM D790 |
| -- 5 | 7270 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 204 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 205 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.41 | ||
| vs. Itself - Static | 0.45 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 1.15 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 104 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 7 | 5.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 400 | J/m | ASTM D4812 |
| 23°C 8 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 5.90 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 260 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 249 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 245 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® CLEAR G 850 Rnew L | Arkema | Nylon 11 | Rilsan® |
| MELOPAS® MP 181.5 | RASCHIG GmbH | Mel Phenolic | MELOPAS® |
| LONGLITE® PBT 6030-200X | CCP Group | PC+PBT | LONGLITE® PBT |
| PETILEN MH 318 | PETKIM Petrokimya Holding A.S. | PP, Unspecified | PETILEN |
| Sylvin 8785-75 Grey 9491 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |