Lumid® HI5001AH
| Category: | Nylon+Olefin , Polyamide + Polyolefin |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hsRc43_Lumid-HI5001AH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumid®HI5001AH is a Polyamide Polyolefin (Nylon Olefin) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is blow molding or injection molding. Lumid®The main features of the HI5001AH are:
Lumid®The typical application fields of HI5001AH are: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/12.5 kg) | 3.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 53.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 320 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 1320 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 6.40 mm) | 48.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm | 250 | J/m | ASTM D256 |
| 23°C, 6.40 mm | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 235 - 250 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 250 - 265 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Extrusion instructions |
|---|
| The processing above is from Blow Molding Process |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P4-20TC-0520 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Hybrid S555 | Ravago Manufacturing Americas, LLC | PC+ABS | Hybrid |
| LNP™ THERMOCOMP™ RC006XXC compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| KMI PP KM-085IB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| Durethan® BKV 50 G H2.0 EF 000000 | LANXESS GmbH | Nylon 6 | Durethan® |