Order Products : sales@su-jiao.com
RTP 3283
| Category: | ETFE , Ethylene Tetrafluoroethylene Copolymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hri0IE_RTP-3283.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ASTM D638 |
| Tensile Strength | 57.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.75 | % | ASTM D638 |
| Flexural Modulus | 13100 | MPa | ASTM D790 |
| Flexural Strength | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 260 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 293 to 332 | °C | |
| Middle Temperature | 293 to 332 | °C | |
| Front Temperature | 293 to 332 | °C | |
| Mold Temperature | 93.3 to 149 | °C | |
| Injection Pressure | 68.9 to 138 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Alcryn® 2060 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| Amilan® CM3004G-30 | Toray Resin Company | Nylon 66 | Amilan® |
| DeWAL DW 224 | DeWAL Industries | PTFE | DeWAL |
| ESTABLEND 0840 GF | Cossa Polimeri S.r.l. | PC+ABS | ESTABLEND |
| HI-ZEX™ 8800B | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |