Kumho ABS HU651
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Korea Kumho Petrochemical Co., Ltd. |
| Trademark: | Kumho ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hreYfS_Kumho-ABS-HU651.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Features: Odorless, High heat resistance Applications: Automobile parts demanding for heat resistance and odorless |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 200°C/21.6 kg | 7.5 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 5.5 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 to 0.80 | % | ASTM D955 |
| -- | 0.50 to 0.80 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 47.6 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 20 | % | ASTM D638 |
| Break | 25 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2010 | MPa | ASTM D790 |
| -- | 2100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 66.0 | MPa | ISO 178 |
| Yield | 62.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 16 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 200 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 150 | J/m | ASTM D256 |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 112 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 104 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 114 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 35.NA | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| MIRASON™ B319 | Mitsui Chemicals, Inc. | LDPE | MIRASON™ |
| GLAMIDE® TY-835TC | TOYOBO America, Inc. | Nylon 66 | GLAMIDE® |
| Indothene LL 20FS020 | Reliance Industries Limited | LLDPE | Indothene LL |
| TECHNYL® A 216 V33 GREY 3067 | Solvay Engineering Plastics | Nylon 66 | TECHNYL® |