Zytel® FR50 NC010A
| Category: | Nylon 66 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hrEvxF_Zytel-FR50-NC010A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% Glass Reinforced, Flame Retardant, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.60 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 0.70 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10600 | 7500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 170 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | -- | % | ISO 527-2 |
| Flexural Modulus | 9450 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 11 | -- | kJ/m² | |
| 23°C | 11 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 40 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 256 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 246 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 261 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.9E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 38 | -- | kV/mm | IEC 60243-1 |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.018 | -- | ||
| 1 MHz | 0.018 | -- | ||
| Comparative Tracking Index (CTI) | PLC 2 | -- | UL 746 | |
| Comparative Tracking Index | 285 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.350 mm | V-0 | -- | ||
| 1.50 mm | V-0 5VA | -- |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.40 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 1660 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.22 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Emission of Organic Compounds | 4.70 | -- | µgC/g | VDA 277 |
| Odor | 4.5 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP553 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| Borealis PE PC0787 | Borealis AG | PE, Unspecified | Borealis PE |
| Sylvin 8200-85 White 1515 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 5132-75 Clear Pink 6233 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9302-70 FUV WHITE 1337 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |