Generic Nylon 610 - Glass Fiber
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hqrmuT_Generic-Nylon-610---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 610 - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.14 - 1.56 | g/cm³ | ASTM D792 |
| 23°C | 1.18 - 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.19 - 0.42 | % | ASTM D955 |
| Transverse flow : 23°C | 0.70 - 1.0 | % | ASTM D955 |
| 23°C | 0.15 - 1.1 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.20 - 0.23 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.29 - 0.61 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 8140 - 12500 | MPa | ASTM D638 |
| 23°C | 4740 - 14500 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Fracture, 23°C | 82.7 - 179 | MPa | ASTM D638 |
| Fracture, 23°C | 107 - 204 | MPa | ISO 527-2 |
| 23°C | 116 - 166 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.5 - 3.5 | % | ASTM D638 |
| Fracture, 23°C | 2.0 - 4.3 | % | ASTM D638 |
| Fracture, 23°C | 2.5 - 5.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3930 - 10900 | MPa | ASTM D790 |
| 23°C | 7110 - 13800 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 121 - 273 | MPa | ASTM D790 |
| 23°C | 195 - 311 | MPa | ISO 178 |
| Coefficient of Friction | 0.18 - 0.71 | ASTM D1894 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 - 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 75 - 100 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 46 - 360 | J/m | ASTM D256 |
| 23°C | 12 - 16 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 370 - 1200 | J/m | ASTM D256 |
| 23°C | 65 - 74 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 210 - 224 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 210 - 220 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 - 218 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 190 - 205 | °C | ISO 75-2/A |
| Melting Temperature | 220 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | |||
| Flow | 2.6E-5 - 4.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.7E-5 - 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 4.0E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (23°C) | 4.6E+2 - 2.5E+14 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.8 - 82.5 | °C | |
| Drying Time | 2.0 - 4.1 | hr | |
| Suggested Max Moisture | 0.16 - 0.20 | % | |
| Rear Temperature | 254 - 275 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 274 - 277 | °C | |
| Processing (Melt) Temp | 256 - 288 | °C | |
| Mold Temperature | 58.6 - 93.3 | °C | |
| Injection Pressure | 96.5 - 103 | MPa | |
| Back Pressure | 0.258 - 0.517 | MPa | |
| Screw Speed | 45 - 55 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 610 - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Dynacom CL6153 | Dynachem Co. Ltd. | PP Copolymer | Dynacom |
| Geon™ Fiberloc™ 80510 | PolyOne Corporation | PVC, Rigid | Geon™ Fiberloc™ |
| Estane® 2103-90AE TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Karina GRAY PVC COMPOUND 812-18/52-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LONGLITE® PBT 7320H-104 | CCP Group | ABS+PBT | LONGLITE® PBT |