Metton® LMR M15XX
| Category: | DCPD , Dicyclopentadiene |
| Manufacturer: | Metton America, Inc. |
| Trademark: | Metton® LMR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hpytaQ_Metton-LMR-M15XX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The Metton LMR reaction injection molding process can provide large parts in low pressure molds with the mechanical property performance similar to injection molded engineering thermoplastics. The combination of Metton LMR's process and material capabilities result in a new design freedom for replacing traditional materials such as metal, wood and fiberglass. Fiber reinforced products tend to have poorer durability, but higher equivalent section modulus. In most semi-structural applications, Metton LMR can be designed to provide equivalent part stiffness for performance and generally at a significant weight reduction. This section contains polymer property data necessary to initially assess the compatibility of Metton LMR with a particular application. The Metton LMR product family includes a standard M15XX product line and a flame-retardant product which meets the requirements for classification as U.L. V-O. The Metton M15XX includes the products M1534, M1537, M1539 and M1540. The Metton V-0 product uses a special three stream RIM injection machine. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.90 | % | |
| Water Absorption (24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 114 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1900 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 46.8 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 4.7 | % | ASTM D638 |
| Flexural Modulus | 1880 | MPa | ASTM D790 |
| Flexural Strength (5.0% Strain) | 70.0 | MPa | ASTM D790 |
| Compressive Strength | 58.4 | MPa | ASTM D695 |
| Shear Strength | 49.5 | MPa | ASTM D732 |
| Poisson's Ratio | 0.39 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 110 | J/m | |
| 23°C | 460 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 108 | °C | ASTM D648 |
| Glass Transition Temperature | > 138 | °C | DMA |
| CLTE - Flow (0 to 50°C) | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sympoxy™ 1225fr/284 | Hapco Inc. | Epoxy | Sympoxy™ |
| Wondel® S GR0 | Nanjing Julong Engineering Plastics Co., LTD | ABS | Wondel® S |
| Abstron SE-22M | Bhansali Engineering Polymers Limited | ABS | Abstron |
| Crastin® SK642FR NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Hifax HKG 418P | LyondellBasell Industries | PP Homopolymer | Hifax |