LNP™ THERMOCOMP™ EC005 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | howStG_LNP-THERMOCOMP-EC005-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* EC005 is a compound based on Polyetherimide resin containing 25% Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound EC-1005 Product reorder name: EC005 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.38 | g/cm³ | ASTM D792 |
| -- | 1.37 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.070 to 0.090 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.50 | % | ISO 294-4 |
| Flow : 24 hr | 0.10 to 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.17 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.27 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 18300 | MPa | ASTM D638 |
| -- | 18200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 200 | MPa | ASTM D638 |
| Break | 200 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.4 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 16300 | MPa | ASTM D790 |
| -- 5 | 16200 | MPa | ISO 178 |
| Flexural Strength 6 | ASTM D790 | ||
| Yield, 50.0 mm Span | 275 | MPa | |
| Break, 50.0 mm Span | 274 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 45 | J/m | ASTM D256 |
| 23°C 7 | 4.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D4812 |
| 23°C 8 | 24 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 10.4 | J | ASTM D3763 |
| 23°C, Total Energy | 11.6 | J | ASTM D3763 |
| -- | 3.00 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 210 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 212 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 204 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 207 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | ASTM D696 |
| Flow : -40 to 40°C | 1.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Transverse : -30 to 30°C | 2.7E-5 | cm/cm/°C | ASTM D696 |
| Transverse : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218 V35 BLACK 34 NG | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| APEX® 3311-75NT | Teknor Apex Company | PVC, Flexible | APEX® |
| ASTALOY™ PC/PET C70H20 | Marplex Australia Pty. Ltd. | PC+PET | ASTALOY™ |
| KPOL-PP K-PPC 1.50 | KPOL Chem Co. | PP Impact Copolymer | KPOL-PP |
| INEOS PP N05U-00 | INEOS Olefins & Polymers USA | PP Impact Copolymer | INEOS PP |