Arnite® T06 200 (extrusion)
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Arnite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hoS5IG_Arnite-T06-200-extrusion-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Arnite® T06 200 (extrusion) is a Polybutylene Terephthalate (PBT) material. It is available in Asia Pacific or Europe for extrusion or injection molding. Primary attribute of Arnite® T06 200 (extrusion): Low Viscosity. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 22.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.45 | % | |
| Equilibrium, 23°C, 50% RH | 0.18 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Thermal Conductivity | 0.11 | W/m/K | |
| Specific Heat Capacity of Melt | 2260 | J/kg/°C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RSV 2 | 2.10 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 3.0 to 12 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | m-cresol, 1g/100ml |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE PMD 50408 | ADDIPLAST | PP Homopolymer | ADDILENE |
| CELEX™ 310HF | Trinseo | PC | CELEX™ |
| Jamplast JPGPPSHH | Jamplast, Inc. | PS (GPPS) | Jamplast |
| LNP™ THERMOCOMP™ ZX08309 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ THERMOCOMP™ |
| 3M™ Dyneon™ PTFE Compound PDR 08004 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |