Electrafil® 1105-10819 NAT
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hn7DAg_Electrafil110510819NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Carbon Fiber |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 255 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 1.7 | % | ASTM D638 |
| Flexural Modulus | 22100 | MPa | ASTM D790 |
| Flexural Strength | 372 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 343 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 335 | °C | ASTM D648 |
| CLTE - Flow | 1.1E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+4 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 - 1.0E+4 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.8 mm) | V-0 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer FEA-251U | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| TRANSMARE® 14CNF30-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Pearlbond™ 508 | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlbond™ |
| Osterlene® LD6521 | Osterman & Company | LDPE | Osterlene® |
| Dow Corning® C6-570 | Dow Corning Corporation | Silicone | Dow Corning® |