LNP™ THERMOCOMP™ DF0049 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hn2XNf_LNPTHERMOCOMPDF0049compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP DF0049 is a compound based on Polycarbonate resin containing Flame Retardant, Glass Fiber. Added features of this material include: Flame Retardant. Also known as: LNP* THERMOCOMP* Compound DF-1004 FR Product reorder name: DF0049 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6630 | MPa | ASTM D638 |
| Tensile Strength (Break) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.8 | % | ASTM D638 |
| Flexural Modulus | 6600 | MPa | ASTM D790 |
| Flexural Strength | 172 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 820 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 143 | °C | ASTM D648 |
| CLTE - Flow (-40 to 40°C) | 2.5E-5 | cm/cm/°C | ASTM E831 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ GA510 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| TOTAL Polyethylene HDPE HL 535 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| DJSilicone NE-661 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| Geon™ Vinyl Rigid Extrusion 87262 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| PMC® 121-50 | Smooth-On, Inc | PUR, Unspecified | PMC® |