Ferro PP MPP40FJ15NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hkpkAy_Ferro-PP-MPP40FJ15NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ferro PP MPP40FJ15NA is a Polypropylene Homopolymer (PP Homopolymer) material filled with 41% mica. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Ferro PP MPP40FJ15NA are:
Typical application of Ferro PP MPP40FJ15NA: Appliances |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.90 | % | |
| Across Flow | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 33.8 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 10 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 3580 | MPa | |
| Tangent : 23°C | 5140 | MPa | |
| Flexural Strength (23°C) | 53.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 150 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 0.452 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 85.0 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 204 to 213 | °C | |
| Middle Temperature | 210 to 216 | °C | |
| Front Temperature | 216 to 218 | °C | |
| Nozzle Temperature | 218 to 227 | °C | |
| Mold Temperature | 43.3 to 57.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vyncolit® BXE7670 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Iupilon® MB5002R | Mitsubishi Engineering-Plastics Corp | PC+Polyester | Iupilon® |
| MAJORIS DG407X - 8784 | AD majoris | PP, Unspecified | MAJORIS |
| ADENE® O07MQE-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |
| Sylvin 8820H Purple 8424 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |