PRE-ELEC® CP 1319
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hkOepQ_PRE-ELEC-CP-1319.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® CP 1319 is a conductive thermoplastic compound based on EVA. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity. PRE-ELEC® CP 1319 has excellent mechanical properties and is easy to extrude. Typical applications include blown mono- or co-extrusion film for ESD bags and innerliners, bags or layflat tubing for hazardous powders. PRE-ELEC® CP 1319 is also suitable for extrusion foam applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/10.0 kg | 4.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 1.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Transverse flow : Yield | 13.1 | MPa | ASTM D638 |
| Flow : Yield | 13.1 | MPa | ASTM D638 |
| Transverse flow : Yield | 13.0 | MPa | ISO 527-2 |
| Flow : Yield | 13.0 | MPa | ISO 527-2 |
| Across Flow | 15.2 | MPa | ASTM D638 |
| Flow | 19.3 | MPa | ASTM D638 |
| -- 1 | 15.0 | MPa | ISO 527-2 |
| -- 2 | 19.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Transverse flow : Yield | 60 | % | ASTM D638, ISO 527-2 |
| Flow : Yield | 70 | % | ASTM D638, ISO 527-2 |
| Transverse flow : Fracture | > 600 | % | ASTM D638 |
| Flow : Fracture | > 600 | % | ASTM D638 |
| Fracture 3 | > 600 | % | ISO 527-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+4 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 200°C |
| Note Message | |
|---|---|
| 1 . | Across Flow |
| 2 . | Flow |
| 3 . | Across Flow |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toraycon® 5107G | Toray Resin Company | PBT | Toraycon® |
| ALTECH® PS A 1000/536 AS WT1113-05 | ALBIS PLASTIC GmbH | PS (HIPS) | ALTECH® PS |
| Comtrex Flexible PVC® 63XCF | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | Comtrex Flexible PVC® |
| Edgetek™ ET3300-5007 Natural FD | PolyOne Corporation | PBT | Edgetek™ |
| OPNYL OP66UT 108 | Ovation Polymers Inc. | Nylon 66 | OPNYL |