Hifax CA 1110 G4 LS/4
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hkDmFp_Hifax-CA-1110-G4-LS-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| "Hifax" CA 1110 G4 LS/4 is a high melt flow, 10% mineral filled, UV stabilised high impact polypropylene copolymer. The grade has been specifically designed for moulding large complex parts that require high impact strength as well as good stiffness. This product has good UV resistance and very good aesthetics and is designed for outdoor application. It is not recommended for painted applications as surface defects could appear after painting. Shrinkage is lower (LS = low shrinkage) compared to Hifax CA 1110 G4. This grade is available in custom colour, pellet form. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 16 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 18.0 | MPa | ISO 527-2 |
| Flexural Modulus | 1150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 4.7 | kJ/m² | |
| -20°C | 5.5 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 73.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 118 | °C | ISO 306/A50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® STAMAX 30YM243 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® STAMAX |
| NILFLEX® SH A40 MC009 | Taro Plast S.p.A. | SEBS | NILFLEX® |
| Ferro PP TPP35AC23NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| IROGRAN® A 70 H 4673 M | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| SCHULAMID® 66 MV HI20 | A. Schulman Inc. | Nylon 66 | SCHULAMID® |