Generic PP Homopolymer - Glass Fiber
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hizyXQ_Generic-PP-Homopolymer---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.953 - 1.26 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 1.0 - 9.9 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.50 - 15 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 1.00 - 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 0.69 | % | ASTM D955 |
| Transverse flow : 23°C | 0.78 - 1.3 | % | ASTM D955 |
| 23°C | 0.18 - 1.0 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.010 - 0.034 | % | ASTM D570 |
| 23°C, 24 hr | 0.047 - 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.096 - 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 97 - 115 | ASTM D785 | |
| Durometer Hardness | |||
| 23°C | 72 - 95 | ASTM D2240 | |
| 23°C | 69 - 85 | ISO 868 | |
| Ball Indentation Hardness | 98.9 - 121 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2000 - 7780 | MPa | ASTM D638 |
| 23°C | 2750 - 10000 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 35.8 - 96.5 | MPa | ASTM D638 |
| Yield, 23°C | 39.9 - 95.6 | MPa | ISO 527-2 |
| Fracture, 23°C | 31.4 - 90.9 | MPa | ASTM D638 |
| Fracture, 23°C | 38.0 - 101 | MPa | ISO 527-2 |
| 23°C | 39.6 - 102 | MPa | ASTM D638 |
| 23°C | 27.0 - 96.6 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 2.9 - 4.1 | % | ASTM D638 |
| Yield, 23°C | 2.4 - 5.1 | % | ISO 527-2 |
| Fracture, 23°C | 1.5 - 7.8 | % | ASTM D638 |
| Fracture, 23°C | 1.5 - 4.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2220 - 7100 | MPa | ASTM D790 |
| 23°C | 2880 - 7830 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 51.4 - 131 | MPa | ASTM D790 |
| 23°C | 76.0 - 144 | MPa | ISO 178 |
| Yield, 23°C | 49.0 - 147 | MPa | ASTM D790 |
| Fracture, 23°C | 82.3 - 142 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 44.8 - 83.1 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.6 - 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 30 - 51 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 41 - 110 | J/m | ASTM D256 |
| 23°C | 6.1 - 14 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 230 - 700 | J/m | ASTM D256 |
| 23°C | 44 - 56 | kJ/m² | ISO 180 |
| Dart Drop Impact (23°C) | 0.300 - 0.922 | J | ASTM D3029 |
| Dart Drop Impact (23°C) | 0.199 - 0.466 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 147 - 163 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 141 - 161 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 128 - 157 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 118 - 155 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 118 - 164 | °C | ASTM D1525 |
| -- | 110 - 166 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 182 - 183 | °C | |
| -- | 165 | °C | ISO 11357-3, ASTM D3418 |
| -- | 160 - 165 | °C | ISO 3146 |
| CLTE - Flow | |||
| -- | 8.0E-6 - 0.068 | cm/cm/°C | ASTM D696 |
| -- | 3.0E-6 - 4.1E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity (23°C) | 0.19 - 0.35 | W/m/K | ASTM C177 |
| RTI Elec | 65.0 - 66.1 | °C | UL 746 |
| RTI Imp | 65.0 - 66.1 | °C | UL 746 |
| RTI | 65.0 - 66.1 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 7.6E+13 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 8.4E+14 - 1.0E+16 | ohms·cm | ASTM D257 |
| 23°C | 1.0E+13 - 2.5E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | |||
| 23°C | 20 - 22 | kV/mm | ASTM D149 |
| 23°C | 59 - 61 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C) | 2.48 - 3.02 | ASTM D150 | |
| Dissipation Factor | |||
| 23°C | 1.0E-3 | ASTM D150 | |
| 23°C | 0.0 - 2.5E-5 | IEC 60250 | |
| Arc Resistance | 120 - 125 | sec | ASTM D495 |
| Comparative Tracking Index | 599 - 650 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 99 - 100 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 550 - 776 | °C | IEC 60695-2-13 |
| Oxygen Index | 20 - 21 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.3 - 82.3 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 203 - 247 | °C | |
| Middle Temperature | 234 - 246 | °C | |
| Front Temperature | 246 - 247 | °C | |
| Nozzle Temperature | 245 - 247 | °C | |
| Processing (Melt) Temp | 228 - 236 | °C | |
| Mold Temperature | 48.0 - 60.0 | °C | |
| Injection Pressure | 85.9 - 205 | MPa | |
| Holding Pressure | 51.0 - 60.3 | MPa | |
| Back Pressure | 0.241 - 0.423 | MPa | |
| Screw Speed | 45 - 75 | rpm | |
| Cushion | 8.81 - 8.93 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2201H0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| TUFNYL® SXXIC GRANITE GREY | SRF Ltd. | Nylon 6 | TUFNYL® |
| Chemlon® 140 M | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Colorite G Series 9812G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| Geon™ Vinyl Flexible R3578A | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |