Color-in™ HAC-M
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | Color-in™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hiwNk9_Color-in-HAC-M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HAC-M is injection a molding aesthetic resin.HAC-M is a color creativity plan.HAC-M is mainly used in appearance items of household appliance,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ASTM D785 | |
| Pencil Hardness - 500g | HB |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Flexural Modulus | 2300 | MPa | ASTM D790 |
| Flexural Strength | 78.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | > 90 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 210 to 240 | °C | |
| Middle Temperature | 220 to 245 | °C | |
| Front Temperature | 230 to 255 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 85.0 to 95.0 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 40 to 55 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUPLENE® R520Y | SK Global Chemical | PP Random Copolymer | YUPLENE® |
| FR-PET® BLR6001MZ | Polyplastics Co., Ltd. | PET | FR-PET® |
| Gallonprene® GP420-7007 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hostacom HYG 343L 356015 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LNP™ STAT-KON™ MFD03 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |