Elastollan® 1180A10
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hib7Ro_Elastollan-1180A10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® 1180A is specifically formulated for extruded profile, sheet and film applications. Elastollan® 1180A exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1180A is rated UL-94 HB in vertical flame test for wall thickness of 0.83 mm. Elastollan® 1180A also conforms to the FDA food contact section, book 21, section 177.2600. Elastollan® 1180A also has NSF Standard 61 "Water Contact Material" certification. Elastollan® 1180A is supplied uncolored in diced or pelletized form. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 20 to 50 | g/10 min | |
| 190°C/8.7 kg | 10 to 20 | g/10 min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 12.4 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 17.2 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 25.0 | mg | ASTM D1044 |
| Abrasion - DIN | 25 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 53 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 6.21 | MPa | |
| 300% Strain | 14.5 | MPa | |
| Tensile Strength | 33.8 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 590 | % | ASTM D412 |
| Tear Strength 1 | 96.3 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 25 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | Internal Method |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.830 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 160 to 200 | °C | |
| Cylinder Zone 3 Temp. | 160 to 200 | °C | |
| Cylinder Zone 5 Temp. | 160 to 200 | °C | |
| Adapter Temperature | 175 to 200 | °C | |
| Die Temperature | 175 to 205 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PBT 30G6F | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| Braskem PP CP 295 | Braskem | PP Impact Copolymer | Braskem PP |
| POLYfill PPH K20020 | Polykemi AB | PP Homopolymer | POLYfill |
| TechnoGreen PP LGF 60-10-04 | TechnoCompound GmbH | PP, Unspecified | TechnoGreen |
| BioBatch 1852 | TechnoCompound GmbH | Biodeg Polymers | BioBatch |