Diamond ASA T-120 is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) 1 | ASTM D1238 | ||
| 200°C/5.0 kg | 0.70 | g/10 min | |
| 230°C/3.8 kg | 2.8 | g/10 min | |
| Molding Shrinkage - Flow | 0.30 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 104 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 47.4 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 3 | 2390 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 92.2 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm | 100 | °C | |
| Vicat Softening Temperature | 123 | °C | ASTM D1525 4 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Suggested Shot Size | 40 to 70 | % | |
| Suggested Max Regrind | 30 | % | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 232 to 265 | °C | |
| Front Temperature | 235 to 272 | °C | |
| Nozzle Temperature | 220 to 272 | °C | |
| Processing (Melt) Temp | 220 to 272 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.517 to 1.03 | MPa |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cheng Yu PP236G1 | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Formolon® 676 | Formosa Plastics Corporation, U.S.A. | PVC, Flexible | Formolon® |
| Generic EnBA | Generic | EnBA | Generic |
| KYOCERA KE-850SH | KYOCERA Chemical Corporation | Epoxy | KYOCERA |
| MAJORIS FFR067 - 5168 | AD majoris | PP, Unspecified | MAJORIS |