Plenco 04311 (Compression) Datasheet,Phenolic,Plastics Engineering Co.-SHANGHAI SUSHENG

Message
PLENCO 04311 is a heat resistant, mineral filled phenolic molding compound offering excellent processability, mechanical strength, and improved cold powder pourability characteristics. UL recognized under component file E40654. 04311 is available in black.

General Information
Filler / Reinforcement	Mineral filler
Features	Workability, good Good strength Heat resistance, high
UL File Number	E40654
Appearance	Black
Forms	Particles
Processing Method	Compression molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.48	g/cm³	ASTM D792
Apparent Density	0.68	g/cm³	ASTM D1895
Molding Shrinkage - Flow	0.33	%	ASTM D955
Water Absorption (24 hr)	0.29	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (E-Scale)	83		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	8790	MPa	ASTM D638
Tensile Strength	54.0	MPa	ASTM D638
Tensile Elongation (Break)	0.60	%	ASTM D638
Flexural Modulus	9180	MPa	ASTM D790
Flexural Strength	78.3	MPa	ASTM D790
Compressive Strength	186	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	19.9	J/m	ASTM D256
Notched Izod Impact	17	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	186	°C	ASTM D648
Continuous Use Temperature	203	°C	ASTM D794
CLTE - Flow	8.2E-5	cm/cm/°C	ASTM E831
Thermal Conductivity (100°C)	0.50	W/m/K	ASTM C177

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	6.9E+12	ohms·cm	ASTM D257
Dielectric Strength ¹	15	kV/mm	ASTM D149
Dielectric Constant (1 MHz)	4.70		ASTM D150
Dissipation Factor (1 MHz)	0.037		ASTM D150
Arc Resistance	166	sec	ASTM D495
Comparative Tracking Index (CTI)	175	V	UL 746

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm)	V-1		UL 94
Oxygen Index	27	%	ASTM D2863

Additional Information
The value listed as Thermal Conductivity, ASTM C177 was tested according to the ASTM E1461 standard.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.17%Heat Resistance, ASTM D794: 203°CDrop Ball Impact, PLENCO Method: 85 J/m

Additional Information

The value listed as Thermal Conductivity, ASTM C177 was tested according to the ASTM E1461 standard.The value listed as Mold Shrink, Linear-Flow, ASTM D955 was tested according to the ASTM D6289 standard.The value listed as Comparative Tracking Index, UL 746 was tested according to ASTM D3638.Post Shrinkage, ASTM D6289, 72hr, 120°C: 0.17%Heat Resistance, ASTM D794: 203°CDrop Ball Impact, PLENCO Method: 85 J/m

Injection	Nominal Value	Unit
Drying Temperature	90.0	°C
Drying Time	0.50	hr
Mold Temperature	165 - 182	°C
Back Pressure	0.300	MPa
Screw Speed	< 60	rpm

Injection instructions
Mold Close Time: 3-8 sec

Note Message
1 .	Method A (short time)

Category:	Phenolic , Phenolic
Manufacturer:	Plastics Engineering Co.
Trademark:	Plenco
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	hi1Csn_Plenco-04311-Compression-.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 300 SI 4	RTP Company	PC	RTP
TAIRIREX HP9450	Formosa Plastics Corporation	PS (HIPS)	TAIRIREX
Dryflex® T40	ELASTO	TPE	Dryflex®
EPAMOULD 770A26	Epaflex Polyurethanes S.R.L.	TPU-Polyether	EPAMOULD
SABIC® LLDPE M200024	Saudi Basic Industries Corporation (SABIC)	LLDPE	SABIC® LLDPE