MALAT 9383GFR200 - 8229
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | AD majoris |
| Trademark: | MALAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hh4Mx0_MALAT-9383GFR200---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MALAT 9383GFR200 - 8229 is a 20 % glass fibre reinforced polybutylene terephthalat, halogen free, intended for injection moulding. Classified V0 according to UL94 norm, MALAT 9383GFR200 - 8229 is available in black but other colours can be provided on request. This technical datasheet is valid for all our compounds MALAT 9383GFR200 - 8229: black or other colours. MALAT 9383GFR200 - 8229 combines high mechanical, thermal and electrical properties with excellent chemical resistance and dimensional stability. APPLICATIONS MALAT 9383GFR200 - 8229 is intended for the injection moulding of electrical components and automotive applications including interior, exterior and electrical and mechanical systems, such as: |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 1.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 4900 | MPa | ISO 178 |
| Flexural Stress 2 | 115 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 27 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 179 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 225 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 23 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-2 | UL 94 | |
| 1.60 mm | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | IEC 60695-2-12 |
| 2.00 mm | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| Back pressure: Moderate |
| Note Message | |
|---|---|
| 1 . | Plate 100x100x2 mm |
| 2 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® VX10-X01 | Toray Resin Company | ABS+PBT | Toyolac® |
| NEFTEKHIM PP 1421H (S38CA) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| EGYPTENE HD 5211 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| EPOXIDUR® EP 3580 | RASCHIG GmbH | Epoxy | EPOXIDUR® |
| NORYL™ PX0888 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |