TECHNYL® 2710ST BLACK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hgiCDH_TECHNYL-2710ST-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66, with very high impact resistance even at low temperature, for injection moulding |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.08 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.9 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.1 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength (Yield) | 50.0 | -- | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | -- | % | ASTM D638 |
| Flexural Modulus | 2200 | -- | MPa | ASTM D790 |
| Flexural Strength (Break) | 70.0 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 950 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 70.0 | -- | °C | ASTM D648 |
| Melting Temperature | 262 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 7.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Heat Deflection Temperature - 0.64 MPa | 222 | -- | °C | ASTM D648 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 30 | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity | 3.20 | 4.00 | IEC 60250 | |
| Dissipation Factor | 0.020 | 0.060 | IEC 60250 | |
| Comparative Tracking Index | IEC 60112 | |||
| Solution A | 575 | 600 | V | |
| Solution B | 450 | -- | V |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 265 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 280 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN2320SB | Ginar Technology Co., LTD. | Nylon 66/6 | Mapex |
| MonoSol® D-7031 XR | MonoSol, LLC | PVOH | MonoSol® |
| Toraypef® 15020 AP5M | Toray Resin Company | Polyolefin, Unspecified | Toraypef® |
| AEI SX-0610:CM601 | AEI Compounds Limited | XLPE | AEI |
| Hostacom ERC 2061N | LyondellBasell Industries | PP, Unspecified | Hostacom |