Stat-Tech™ PP-16CP/000 2 HI BLACK
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hgFSh2_Stat-Tech-PP-16CP-000-2-HI-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Stat-Tech™ electrically conductive compounds are specifically engineered to provide anti-static, ESD and RFI/EMI shielding performance for critical electronic applications. These compounds combine the performance of select engineering resins with reinforcing additives such as carbon powder, carbon fiber, nickel-coated carbon fiber and stainless steel fiber for low to high levels of conductivity depending upon application requirements. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.80 to 1.0 | % | |
| Across Flow | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 25.5 | MPa | ASTM D638 |
| Tensile Elongation 1(Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 1690 | MPa | ASTM D790 |
| Flexural Strength | 42.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 320 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 3.18 mm | 98.0 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 50.0 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+3 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+3 to 1.0E+5 | ohms·cm | ASTM D257 |
| Static Decay - (Mil-B-81705C), 12% RH, 5000 kV to 50 kV | 2 | msec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 199 to 221 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6091-55A BLACK | RTP Company | TPV | RTP |
| S&E Footwear G-04-036ESD | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E Footwear |
| TAISOX 3224 | Formosa Plastics Corporation | LLDPE | TAISOX |
| Ateva® 2803G | Celanese EVA Performance Polymers | EVA | Ateva® |
| Sylvin 9302-75 FU WHITE 1279 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |