Elastollan® 1160 A 13 P 000
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hgDCIi_Elastollan-1160-A-13-P-000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyether-Polyurethane with outstanding hydrolysis resistance, low temperature flexibility and high resistance to micro-organisms, plasticized, phthalate-free. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 60 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 70.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 1.00 | MPa | DIN 53504-S2 |
| 100% strain | 2.50 | MPa | DIN 53504-S2 |
| 300% strain | 4.50 | MPa | DIN 53504-S2 |
| Tensile Strength | 27.0 | MPa | DIN 53504-S2 |
| Tensile Elongation (Break) | 850 | % | DIN 53504-S2 |
| Tear Strength 1 | 40 | kN/m | ISO 34-1 |
| Compression Set (23°C, 72 hr) | 25 | % | ISO 815 |
| Additional Information |
|---|
| The plaques are manufactured by injection moulding from pre-dried granules (water content less 0,02%). Test paques are aged 20 hrs at 100°C.Specimens are cut from test plaques. The test conditions: 23°C ± 2°C and 50% ± 6% rel. humidity. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 195 | °C | |
| Front Temperature | 185 - 195 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 185 - 195 | °C | |
| Mold Temperature | 20.0 - 40.0 | °C | |
| Injection Rate | Slow |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp DBS8613 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Anjacom® 055/80-GF5 | Almaak International GmbH | PC+ABS | Anjacom® |
| Carbo-Rite™ F-1260 | Lubrizol Advanced Materials, Inc. | Acetal (POM) Copolymer | Carbo-Rite™ |
| CP PRYME® PC/ABS PCA100 | Chase Plastics Services Inc. | PC+ABS | CP PRYME® PC/ABS |
| Fainplast PVC RH 207/OP | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |