SCHULAMID® 612 IC 4005 W
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hfSiXX_SCHULAMID-612-IC-4005-W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unfilled and plasticized nylon 612 compound |
| General Information | |
|---|---|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 480 | 275 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | |||
| Yield | 21.0 | 22.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 41.0 | 33.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 12 | 46 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 240 | 240 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 485 | -- | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | |||
| 3.5% strain | 13.0 | -- | MPa | ISO 178 |
| 10% strain | 18.0 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -40°C | 25 | -- | kJ/m² | ISO 179/1eA |
| -30°C | 30 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 120 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -40°C | No Break | -- | ISO 179/1eU | |
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 95.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 40.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 189 | -- | °C | ISO 306/A50 |
| -- | 120 | -- | °C | ISO 306/B50 |
| Additional Information |
|---|
| 干燥 ISO 1874-PA 612-P-EAGHLW-14-005-XDIN73378-PA 612-HIPHL |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RHX200 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| SCANAMID 6 B12^ F20 | Polykemi AB | Nylon 6 | SCANAMID 6 |
| THERMOLAST® K TF6PEN (Series: FC/AD/PE) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Ultradur® B 6550 FC | BASF Corporation | PBT | Ultradur® |
| Bapolan® 6403 | Bamberger Polymers, Inc. | PS (HIPS) | Bapolan® |