| EPO-TEK® H31LV is a single component, silver-filled, electrically conductive epoxy designed for semiconductor die attach applications found in hybrids, JEDEC, and opto-electronic packaging. Low viscosity version of EPO-TEK® H31. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Ion Type | |||
| Cl- | 14 | ppm | |
| K+ | 47 | ppm | |
| Na+ | 380 | ppm | |
| NH4+ | 8 | ppm | |
| Particle Size | < 45.0 | µm |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 387 | °C | TGA |
| Die Shear Strength - >5 kg (23°C) | 11.7 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 200 | °C | |
| Intermittent | -55 to 300 | °C | |
| Storage Modulus (23°C) | 1.77 | GPa | |
| Thixotropic Index | 1.80 | ||
| Weight Loss on Heating | |||
| 200°C | 0.13 | % | |
| 250°C | 0.27 | % | |
| 300°C | 1.1 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 110 | °C | |
| CLTE - Flow | |||
| -- 2 | 2.6E-5 | cm/cm/°C | |
| -- 3 | 1.5E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.55 | W/m/K |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shelf Life 4 | 26 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | Silver | ||
| Density | 1.57 | g/cm³ | |
| Viscosity 5(23°C) | 2.0 to 3.5 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 4300 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 85 | ||
| Lap Shear Strength (23°C) | 9.65 | MPa | |
| Volume Resistivity (23°C) | < 8.0E-3 | ohms·cm |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-250°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Refrigerated |
| 5 . | 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® SJ9400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| SEQUEL® 1718-UV RXF | LyondellBasell Industries | Polyolefin, Unspecified | SEQUEL® |
| Nypol® PA A3 ST HS PRTA011 NR365 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Gebalon PC ULtimate G20 FR(y) | geba Kunststoffcompounds GmbH | PC | Gebalon |
| OnFlex™ S KG 60A-3S2018 | PolyOne Corporation | TPE | OnFlex™ |