| 82 Shore D Standard Performance Polyester Elastomer |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/2.16 kg) | 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (240°C/2.16 kg) | 11.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.6 | % | |
| Flow | 1.6 | % | |
| Water Absorption | |||
| 24 hr | 0.30 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 76 | ||
| Shore D, 15 sec | 70 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1180 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 36.0 | MPa | |
| Break | 46.0 | MPa | |
| 10% Strain | 34.0 | MPa | |
| 50% Strain | 28.0 | MPa | |
| 100% Strain | 26.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 19 | % | |
| Break | > 300 | % | |
| Nominal Tensile Strain at Break | 340 | % | ISO 527-2 |
| Flexural Modulus | 1150 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 210 | kN/m | |
| Flow | 230 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 5.0 | kJ/m² | |
| -30°C | 5.0 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 5.5 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Tensile Impact Strength (23°C) | 57.0 | kJ/m² | ISO 8256/1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Brittleness Temperature | -84.0 | °C | ISO 974 |
| Glass Transition Temperature 1 | 50.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 213 | °C | ISO 306/A50 |
| -- | 150 | °C | ISO 306/B50 |
| Melting Temperature 2 | 221 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.5E-4 | cm/cm/°C | |
| Transverse | 1.5E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 21 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.00 | ||
| 1 MHz | 3.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.010 | ||
| 1 MHz | 0.018 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 0.910 mm | HB | ||
| 1.50 mm | HB | ||
| Oxygen Index | 22 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.13 | g/cm³ | |
| Specific Heat Capacity of Melt | 2150 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.15 | W/m/K |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt | |
| Emission of Organic Compounds | 240 | µgC/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taipol 7131 | TSRC Corporation | SEBS | Taipol |
| AKROMID® B3 GF 60 black (2497) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| ESTADIENE 2506 | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Hyundai EP PA66 LD240 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |
| Sylvin 8310-75C UV White 1507 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |