TAROLON 2500 W X0
| Category: | PC , Polycarbonate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hecwNR_TAROLON-2500-W-X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate medium viscosity, self extinguishing UL 94 V0. UL94 V0 approved all colors @ 0,97 mm. UL746B approved. Available: all colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 to 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 to 0.70 | % | |
| Across Flow | 0.50 to 0.70 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.10 | % | ASTM D570, ISO 62 |
| Saturation | 0.35 | % | ASTM D570 |
| Saturation, 23°C | 0.35 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 70.0 | MPa | |
| Break | 60.0 | MPa | |
| Tensile Elongation (Break) | 80 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 95.0 | MPa | ISO 178 |
| -- 2 | 90.0 | MPa | ISO 178 |
| Yield | 95.0 | MPa | ASTM D790 |
| Break | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 30 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 4(23°C) | 300 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 600 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 138 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 75.0 | °C | UL 746B |
| -- 5 | 120 | °C | IEC 60216 |
| Vicat Softening Temperature | 152 | °C | ISO 306/A50, ASTM D1525 6 |
| Ball Pressure Test (125°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 200 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 34 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 90.0 to 110 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Break |
| 3 . | 6x4x50 mm |
| 4 . | 6x4x50 mm |
| 5 . | 20000 hrs |
| 6 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N63B | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Spartech Polycom SC7-70922 | Spartech Polycom | PC | Spartech |
| Sylvin 8200-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Ferro PP LPP30BK85HB | Ferro Corporation | PP Copolymer | Ferro PP |
| Geon™ Vinyl Flexible 90201 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |