ATTANE™ 4607G
| Category: | ULDPE , Ultra Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ATTANE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | he6mlg_ATTANE-4607G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ATTANE™4607G ultra-low density polyethylene copolymer is used as a surface film in the cast film, which has excellent low-temperature thermal adhesion properties and excellent tear strength and impact strength. In tensile film applications, ATTANE™4607G ultra-low density polyethylene copolymer shows excellent tensile properties as well as good physical properties and adhesion properties. ATTANE™4607G ultra-low density polyethylene copolymer can be used in the co-extrusion process of blown film. In this process, the excellent film bubble stability of the product after mixing with other resins makes ATTANE™4607G ultra-low density polyethylene copolymer can be used as a sealant in thin film multilayer structures. Application field:
Meet the following regulatory requirements:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.904 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Puncture Energy (23 µm) | 5.00 | J | Internal method |
| Film Puncture Force (23 µm) | 48.0 | N | Internal method |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm | 4.30 | MPa | ISO 527-3 |
| TD : Yield, 23 µm | 3.60 | MPa | ISO 527-3 |
| MD : Break, 23 µm | 33.0 | MPa | ISO 527-3 |
| TD : Break, 23 µm | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm | 500 | % | ISO 527-3 |
| TD : Break, 23 µm | 630 | % | ISO 527-3 |
| Dart Drop Impact (23 µm) | 180 | g | ISO 7765-1/A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 23 µm | 190 | g | ASTM D1922 |
| TD : 23 µm | 390 | g | ASTM D1922 |
| Unstretched bond | 130 | g | ASTM D4649 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 72.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm) | 92 | ASTM D2457 | |
| Haze (23.0 µm) | 0.70 | % | ASTM D1003 |
| Additional Information |
|---|
| 对于在 Lab Collin 生产线上采用 15 米/分冷却辊于 25°C 下生产的单层薄膜所测量的薄膜属性。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 260 | °C |
| Extrusion instructions |
|---|
| 铸造薄膜挤出的制造条件： 熔体温度：190 - 260 °C 建议的厚度范围：10 - 60 µm 脱离速度：150 - 300 米/分 冷却辊温度：20 - 60 °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NITRIFLEX PDC-7421 | NITRIFLEX | PVC+NBR | NITRIFLEX |
| Cheng Yu PP230H | Cheng Yu Plastic Company Limited | PP, Unspecified | Cheng Yu |
| Durez® 7716 | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| ELASTOSIL® E 50 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| Sylvin 8280-70UV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |