Kepital® F20-52G
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | KEP Americas |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hdoG5O_Kepital-F20-52G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low gloss, UV resistance, easy-flow grade for general injection molding. F20-52G is suited for parts requiring a good weather resistance and low gloss characteristic. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 10 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 58.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 40 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2350 | MPa | ISO 178 |
| Flexural Stress (23°C) | 78.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 6.0 | kJ/m² | ISO 179/1eA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECNOBLEND B52 | Taro Plast S.p.A. | ABS+Nylon | TECNOBLEND |
| Network Polymers PP PPB 25 0110 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| Comco Lube | Comco-Plastic GmbH | Nylon, Unspecified | Comco |
| INDURE™ X225 | LyondellBasell Industries | Polyolefin, Unspecified | INDURE™ |
| Karina IVORY PVC COMPOUND 807D35/ 1-CY-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |