Wanthane® WHT-8195RV
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Wanhua Chemical Group Co., Ltd. |
| Trademark: | Wanthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hdOIBO_WanthaneWHT8195RV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYPE: Polyether-based grade Extrusion and injection molding grade FEATURES: Excellent hydrolytic stability, fungus resistance, good low-temperature flexibility, complies with FDA(21 CFR 177.1680, 177.2600), ROHS, ISO 10993 & USP VI Applications: Electronic parts, wire & cable, medical products, etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| DIN Abrasion | 75.0 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 12.0 | MPa | ASTM D412 |
| 300% strain | 25.0 | MPa | ASTM D412 |
| Tensile Strength (Break) | 38.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 380 | % | ASTM D412 |
| Tear Strength | 120 | kN/m | ASTM D624 |
| Compression Set | ASTM D395 | ||
| 23°C, 24 hr | 28 | % | ASTM D395 |
| 70°C, 22 hr | 70 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D3418 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 200 | °C | |
| Middle Temperature | 205 | °C | |
| Front Temperature | 210 | °C | |
| Nozzle Temperature | 215 | °C | |
| Mold Temperature | 23 | °C | |
| Screw L/D Ratio | 25.0:1.0 to 30.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Cylinder Zone 1 Temp. | 200 | °C | |
| Cylinder Zone 2 Temp. | 205 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Cylinder Zone 4 Temp. | 215 | °C | |
| Adapter Temperature | 220 | °C | |
| Die Temperature | 215 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ST7400-5006 Natural AS | PolyOne Corporation | PS (HIPS) | Stat-Tech™ |
| Axiall PVC 8833 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| CYCOLOY™ C1200HF resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |
| Petrothene® NA831000 | LyondellBasell Industries | LDPE | Petrothene® |
| Akulon® Ultraflow K-FKG6 | DSM Engineering Plastics | Nylon 6 | Akulon® Ultraflow |