MAJORIS DW434X/8
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hcgNnT_MAJORIS-DW434X-8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS DW434X/8 is a high performance reinforced polypropylene compound intended for injection moulding. APPLICATIONS MAJORIS DW434X/8 is intended for components that require good impact strength, rigidity and dimensional stability. Suitable applications are:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.95 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 81.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.2 | % | ISO 527-2 |
| Flexural Modulus 1 | 10400 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 2.4 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 20 | kJ/m² | ISO 179/1eU |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 200 - 220 | °C | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-065 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| Ultramid® A3EG7 | BASF Corporation | Nylon 66 | Ultramid® |
| IDI BMC B30 (Glass Content 20%) | IDI Composites International | TS, Unspecified | IDI BMC |
| Lucofin® 1411-t2 | Lucobit AG | Polyolefin, Unspecified | Lucofin® |
| POLYfill PP CCP20020 UV | Polykemi AB | PP, Unspecified | POLYfill |