SCHULAMID® 6 MT 25 FR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hbgAdM_SCHULAMID-6-MT-25-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 25% mineral filled flame-retardant Polyamide 6 compound with low warpage; halogen free |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 7300 | 2100 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 80.0 | 27.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.5 | 63 | % | ISO 527-2/1A/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 4.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 32 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 120 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 215 | -- | °C | ISO 306/A50 |
| -- | 200 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | -- | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 525 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | ISO 3795 | |||
| 0.750 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 1.50 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 3.00 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.750 mm | V-2 | -- | ||
| 1.50 mm | V-2 | -- | ||
| 3.00 mm | V-2 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.750 mm | 700 | -- | °C | |
| 1.50 mm | 700 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VAMPLEN A 0023 C V2 | Vamp Tech | PP Copolymer | VAMPLEN |
| Colorite CS Series CS7566LS | Colorite Polymers | PVC, Flexible | Colorite CS Series |
| Fiberfil® PP-62/MI/25 | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| Hostacom ERC 213N | LyondellBasell Industries | PP Copolymer | Hostacom |
| 3M™ Dyneon™ Fluoroelastomer FC 2144 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |