EMERGE™ PC 8702-5
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | haxM2S_EMERGE-PC-8702-5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8702-5 Advanced Resin is an ignition-resistant, 20% glass reinforced, polycarbonate resin. This resin contains no bromine, chlorine, or phosphate additives. The resin is designed to meet the German norm DIN VDE-0472 on halogens. It is a medium flow PC resin with a mold release system, intended for injection molding applications. EMERGE ™ PC 8702-5 has a UL 94 V-0 rating at 1.5 mm, 5VA rating at 3.0 mm and V2 rating at 0.75 mm. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.33 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ISO 527-2/50 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 100 | MPa | |
| Break | 90.0 | MPa | |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | 5500 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 8.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 143 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| Ball Indentation Temperature | > 135 | °C | IEC 60335-1 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.5E-5 | cm/cm/°C | |
| Transverse | 5.2E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength (1.60 mm) | 27 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 1.60 mm, 10 Hz | 3.10 | ||
| 1.60 mm, 1 MHz | 3.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 10 Hz | 5.0E-3 | ||
| 100 Hz | 2.5E-3 | ||
| 1 MHz | 0.016 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1 | UL 94 | ||
| 0.750 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 5VA | ||
| Glow Wire Flammability Index 2 | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature 3 | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 3.00 mm | 850 | °C | |
| Oxygen Index 4 | 35 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 GV 20 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Fainplast PVC PK 100 | Fainplast Compounds S.r.l | PVC, Semi-Rigid | Fainplast PVC |
| HiFill® PEEK CF10 A | Techmer Engineered Solutions | PEEK | HiFill® |
| PermaStat® 100 LE | RTP Company | PP, Unspecified | PermaStat® |
| Petrothene® LR590005 | LyondellBasell Industries | HDPE, HMW | Petrothene® |