STYRON™ 6500
| Category: | PS (IRPS) , Ignition Resistant Polystyrene Resin |
| Manufacturer: | Trinseo |
| Trademark: | STYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ha6o92_STYRON-6500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
STYRON™ 6500 is an ignition-resistant polystyrene resin with excellent balance of strength, heat resistance and flow properties that are tailor-made for consumer electronics applications. It is a non-deca ignition resistant polystyrene which is free from polybrominated diphenyl ether (PBDPE) and polybrominated biphenyl (PBB). It is designed for injection molding application. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, Compression Molded | 17.2 | MPa | |
| Yield, Injection Molded | 20.7 | MPa | |
| Break, Compression Molded | 13.8 | MPa | |
| Break, Injection Molded | 19.3 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Break, Compression Molded | 30 | % | |
| Break, Injection Molded | 40 | % | |
| Flexural Modulus | ASTM D790 | ||
| Compression Molded | 1990 | MPa | |
| Injection Molded | 2370 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Compression Molded | 33.8 | MPa | |
| Injection Molded | 40.7 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, Compression Molded | 64 | J/m | |
| 23°C, Injection Molded | 80 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| CLTE - Flow | 7.6E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1(1.50 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-081A-15B | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| RheTech Polypropylene GC20P100-00UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| EVERLON® TC-95C | Ever Polymer Co., Ltd. | SEBS | EVERLON® |
| Generic PBT - Glass Bead\Glass Fiber | Generic | PBT | Generic |
| PLEXIGLAS® Sheet Clear 2890 | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |