Gebablend 65 HI
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | geba Kunststoffcompounds GmbH |
| Trademark: | Gebablend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hZamKq_Gebablend-65-HI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS type with enhanced high impact unnotched and notched impact strength Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 23.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.45 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1/1 |
| Tensile Stress (Yield) | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 35 | kJ/m² | |
| 23°C | 45 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 122 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 to 100 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 250 to 270 | °C | |
| Front Temperature | 250 to 280 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TRANSMARE® 19HNF30-0.001 | Transmare Compounding B.V. | PP Homopolymer | TRANSMARE® |
| HAIPLEN EP90 T8 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Pibiter® HI C3311 NERO900 | SO.F.TER. SPA | PBT | Pibiter® HI |
| Hostacom PPU X9067HS D62813 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Lifoflex® UV FLAM 90700 | Müller Kunststoffe GmbH | TPE | Lifoflex® |