LNP™ LUBRILOY™ K2000XXH compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hZL0Dg_LNP-LUBRILOY-K2000XXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* K2000XXH is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material are: Wear Resistant, Healthcare. Also known as: LNP* LUBRILOY* Compound K Product reorder name: K2000XXH |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 2.2 | % | ASTM D955, ISO 294-4 |
| Across Flow : 24 hr | 2.3 | % | ASTM D955 |
| Across Flow : 24 hr | 2.1 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.33 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2560 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 55.5 | MPa | ASTM D638 |
| Yield | 60.9 | MPa | ISO 527-2 |
| Break | 51.8 | MPa | ASTM D638 |
| Break | 59.9 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 9.3 | % | ASTM D638 |
| Yield | 9.0 | % | ISO 527-2 |
| Break | 32 | % | ASTM D638 |
| Break | 13 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2430 | MPa | ASTM D790 |
| -- | 2420 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 84.1 | MPa | ASTM D790 |
| -- | 65.6 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.38 | ||
| vs. Itself - Static | 0.24 | ||
| Wear Factor - Washer | 10.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 69 | J/m | ASTM D256 |
| 23°C 2 | 6.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1400 | J/m | ASTM D4812 |
| 23°C 3 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.41 | J | ASTM D3763 |
| -- | 0.820 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 159 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 87.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RX® 640 | Sumitomo Bakelite North America, Inc. | Phenolic | RX® |
| Titacon® GB920 | Titan Plastics Compounds Co., Ltd. | Acetal (POM) Copolymer | Titacon® |
| Witcom PA66 3C | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Latamid 66 H2 G/25-V0KB | LATI S.p.A. | Nylon 66 | Latamid |
| LNP™ LUBRICOMP™ UCP36S compound | SABIC Innovative Plastics | PPA | LNP™ LUBRICOMP™ |