Sunny® PC-PBT EN120
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Guangdong Shunde Shunyan New Material Co., Ltd. |
| Trademark: | Sunny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hYrlSO_Sunny-PC-PBT-EN120.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EP reinforced polycarbonate-polybutylene terephthalate |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 1.32 | g/cm³ | ASTM D792 |
| 23°C | 1.32 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.40 to 0.70 | % | ASTM D955 |
| 23°C | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| Equilibrium, 23°C | 0.080 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.080 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- 2 | 100 | MPa | ASTM D638 |
| -- | 100 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 4.7 | % | ASTM D638 |
| Break | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span | 5820 | MPa | ASTM D790 |
| 50.0 mm Span | 6000 | MPa | ISO 178 |
| Flexural Strength | |||
| 50.0 mm Span | 160 | MPa | ASTM D790 |
| -- 4 | 165 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 210 | J/m | ASTM D256 |
| 23°C | 20 | kJ/m² | ISO 180/1A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 240 | °C | |
| Processing (Melt) Temp | 250 | °C | |
| Mold Temperature | 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® B220MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| DENILUB Y 00U 0Si M | Vamp Tech | Nylon 66 | DENILUB |
| FHR EPS R-MER II® 5627 (1.25 lb/ft³) | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| INEOS PP 200-CA25 | INEOS Olefins & Polymers Europe | PP Random Copolymer | INEOS PP |
| LNP™ THERMOCOMP™ RF006EUC compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |