AKROMID® A3 GF 15 1 L black (4673)
| Category: | Nylon 66+PP , Polyamide 66 + PP |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hYpGtN_AKROMID-A3-GF-15-1-L-black-4673-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 GF 15 1 L black (4673) is a 15% glass fibre reinforced and heat stabilised polyamide-blend with a reduced density compared to standard PA66 GF 15 Applications are mainly technical components in the automotive and electronic industry, where a weight and cost reduction is required |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 14.0 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 117 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 1.0 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 1.5 | -- | % | ISO 1110 |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Reinforcement Content | 15 | -- | % | ISO 1172 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5300 | 4000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | 75.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.4 | 5.3 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 7.0 | 7.0 | kJ/m² | |
| 23°C | 10 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 61 | 61 | kJ/m² | |
| 23°C | 68 | 56 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 262 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 2(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (0.800 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.800 mm) | 725 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 10 K/min, DSC |
| 2 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 203A MS | RTP Company | Nylon 6 | RTP |
| API PS 645-21 | American Polymers, Inc. | PS (HIPS) | API PS |
| LARIPUR® LPR 7015 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| LNP™ LUBRICOMP™ DFL12 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ LUBRICOMP™ |
| NORYL™ GFN1F resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |