Braskem PE IP2418
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hYoNZN_Braskem-PE-IP2418.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Good processability, high fluidity, flexibility and mechanical strength. It does not contain additives. Application: Injection molding and blends with EVA for foams. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 24 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 2.00 mm, 10% Igepal, Compression Molded, F50) | 1.00 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 49 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 9.00 | MPa | ASTM D638 |
| Fracture, molding | 8.00 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 160 | % | ASTM D638 |
| Apparent Bending Modulus | 320 | MPa | ASTM D747 |
| Flexural Modulus - 1% Secant (Compression Molded) | 300 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 82.0 | °C | ASTM D1525 1 |
| Injection instructions |
|---|
| Recommended processing conditions for:Blends with EVA: Temperature profile: 100 to 150°C. Injection molding: Temperature profile: 120 to 180°C. |
| Note Message | |
|---|---|
| 1 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Compoceran AC156 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Compoceran |
| DIALAC® TW25 | UMG ABS, Ltd. | ASA | DIALAC® |
| Fusabond® C250 | DuPont Packaging & Industrial Polymers | EVA | Fusabond® |
| Greenflex® ML 60 | Versalis S.p.A. | EVA | Greenflex® |
| LNP™ THERMOCOMP™ ZX08309 compound | SABIC Innovative Plastics Asia Pacific | PPE+PS | LNP™ THERMOCOMP™ |