Order Products : sales@su-jiao.com
KIBILAC® PW-978B
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | KIBILAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hYOnci_KIBILAC-PW-978B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| KIBILAC® PW-978B is an Acrylonitrile Styrene Acrylate (ASA) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: rohs compliant. |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 12.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 88.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 49.0 | MPa | ISO 527-2/50 |
| Break | 38.0 | MPa | ISO 527-2/50 |
| 3.18 mm 1 | 46.1 | MPa | ASTM D638 |
| Tensile Strain (Break) | 20 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 1900 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.35 mm 3 | 66.7 | MPa | ASTM D790 |
| -- 4 | 67.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 250 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 110 | J/m | ASTM D256 |
| -- | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.35 mm 5 | 93.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 94.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 6.35 mm 6 | 103 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 108 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 113 | °C | ASTM D1525 7 |
| -- | 114 | °C | ISO 306/A50 |
| -- | 115 | °C | ISO 306/A120 |
| -- | 100 | °C | ISO 306/B50 |
| -- | 104 | °C | ISO 306/B120 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss | 97 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 95.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 240 to 260 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 4.90 to 6.86 | MPa | |
| Holding Pressure | 3.92 to 5.88 | MPa | |
| Back Pressure | 0.490 to 1.47 | MPa |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 120°C/hr |
| 6 . | 120°C/hr |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2385 A | RTP Company | PUR, Unspecified | RTP |
| Sinvicomp SIZ5305 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Hyundai EP Barrier E100P-R/Natural | HYUNDAI EP Co., Ltd. | Polyolefin, Unspecified | Hyundai EP Barrier |
| PELPRENE™ P150B-05 | TOYOBO America, Inc. | TPEE | PELPRENE™ |
| Sylvin 3230-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |