IROGRAN® A 92 P 4637
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Huntsman Corporation |
| Trademark: | IROGRAN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hY4qEa_IROGRAN-A-92-P-4637.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
IROGRAN A 92 P 4637 is a thermoplastic polyether-polyurethane for injection moulding and extrusion applications. Additional characteristics of the product are excellent microbial resistance, high low-temperature flexibility, especially suitable for cable jacket. PERFORMANCE FEATURES
APPLICATIONS For the production of jacket material for cables, jackets for high pressure hosesspiral hoses, profiles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.13 | g/cm³ | |
| Melt Volume-Flow Rate (MVR) (190°C/21.6 kg) | 55.0 | cm³/10min | |
| Molding Shrinkage | |||
| Flow | 0.40 | % | ASTM D955 |
| -- | 0.90 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, Injection Molded | 92 | ||
| Shore D, Injection Molded | 39 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion 2 | 30 | mm³ | ISO 4649 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | |||
| 100% Strain | 8.96 | MPa | ASTM D412 |
| 100% Strain | 9.10 | MPa | DIN 53504 |
| 300% Strain | 14.1 | MPa | ASTM D412 |
| 300% Strain | 15.9 | MPa | DIN 53504 |
| Tensile Strength 4 | |||
| Break | 33.6 | MPa | ASTM D412 |
| Break | 45.0 | MPa | DIN 53504 |
| Tensile Elongation 5 | |||
| Break | 670 | % | ASTM D412 |
| Break | 600 | % | DIN 53504 |
| Tear Strength 6 | |||
| -- | 116 | kN/m | ASTM D624 |
| -- | 74 | kN/m | ISO 34-1 |
| Compression Set 7 | ASTM D395, ISO 815 | ||
| 23°C, 24 hr | 25 | % | |
| 70°C, 24 hr | 41 | % | |
| Bayshore Resilience | 34 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Hot Air Dryer | 80.0 to 90.0 | °C | |
| Drying Time | |||
| -- | 3.0 | hr | |
| Hot Air Dryer | 3.0 | hr | |
| Dew Point | -30.0 | °C | |
| Rear Temperature | 175 to 195 | °C | |
| Middle Temperature | 175 to 195 | °C | |
| Front Temperature | 175 to 195 | °C | |
| Nozzle Temperature | 180 to 200 | °C | |
| Processing (Melt) Temp | 170 to 195 | °C | |
| Mold Temperature | 20.0 to 70.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 | hr | |
| Hopper Temperature | 25.0 to 40.0 | °C | |
| Cylinder Zone 1 Temp. | 165 to 190 | °C | |
| Cylinder Zone 2 Temp. | 165 to 190 | °C | |
| Cylinder Zone 3 Temp. | 165 to 190 | °C | |
| Cylinder Zone 4 Temp. | 165 to 190 | °C | |
| Cylinder Zone 5 Temp. | 165 to 190 | °C | |
| Adapter Temperature | 175 to 195 | °C | |
| Die Temperature | 175 to 200 | °C |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| 3 . | Injection Molded |
| 4 . | Injection Molded |
| 5 . | Injection Molded |
| 6 . | Injection Molded |
| 7 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rynite® 530 BK503 | DuPont Performance Polymers | PET | Rynite® |
| RheTech Thermoplastic Polyolefin FT4802-01UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| Ultradur® B 6550 | BASF Corporation | PBT | Ultradur® |
| ALCOM® PP 620/10 GY1464-04MCF | ALBIS PLASTIC GmbH | PP Homopolymer | ALCOM® PP |
| Petrothene® M2520FNx02 | LyondellBasell Industries | LDPE | Petrothene® |