Zhongfa PC G2810
| Category: | PC , Polycarbonate |
| Manufacturer: | Yuyao Zhongfa Engineering Plastics Co. Ltd. |
| Trademark: | Zhongfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hXOnBr_Zhongfa-PC-G2810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Zhongfa PC G2810 is a polycarbonate (PC) material, which contains a 10% glass fiber reinforced material. This product is available in the Asia-Pacific region and is processed by injection molding. The main features of Zhongfa PC G2810 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.20 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.13 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 6.5 | % | ASTM D638 |
| Flexural Modulus | 3350 | MPa | ASTM D790 |
| Flexural Strength | 115 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 149 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 4.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | UL 94 | |
| 3.20 mm | V-1 | UL 94 |
| Additional Information |
|---|
| Flexural Modulus, ASTM D790: 3300 to 3400 MPaFlexural Strength, ASTM D790: 110 to 120 MPaHDT at 264 psi, ASTM D648: 142 to 144°CHDT at 66 psi, ASTM D648: 148 to 150°CNotched Izod Impact, ASTM D256: 12 to 17 kJ/m²Tensile Elongation, ASTM D638: 6 to 7%Tensile Strength, ASTM D638: 70 to 80 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 - 110 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Processing (Melt) Temp | 210 - 255 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 70.0 - 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Topilene® J440 | Hyosung Corporation | PP Impact Copolymer | Topilene® |
| Tygon B-44-3 | Saint Gobain - Norton | PVC, Unspecified | Tygon |
| UNISOFT TPE™ ST-45A-BK-1-01 | UNITED SOFT PLASTICS, Inc. | SEBS | UNISOFT TPE™ |
| Karina IVORY PVC COMPOUND -E 500-35/ 1-Y | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| MTEGRITY™ LLDPE LL106AA | M. Holland Company | LLDPE | MTEGRITY™ LLDPE |