Premi-Ject® 1102H
| Category: | TS, Unspecified , Thermoset, Unspecified |
| Manufacturer: | Premix, Inc. |
| Trademark: | Premi-Ject® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hWlB4V_Premi-Ject-1102H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Premi-Ject® 1102H is a fiberglass reinforced thermoset bulk molding compound for coil encapsulation applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 1.85 to 1.95 | g/cm³ | |
| Molding Shrinkage - Flow | 0.050 to 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9000 | MPa | ASTM D638 |
| Tensile Strength | 26.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.40 | % | ASTM D638 |
| Flexural Modulus | 9000 | MPa | ASTM D790 |
| Flexural Strength | 68.0 | MPa | ASTM D790 |
| Poisson's Ratio | 0.30 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 380 | J/m | ASTM D256 |
| Unnotched Izod Impact | 430 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 200 | °C | ASTM D648 |
| CLTE | |||
| Flow 1 | 2.5E-5 | cm/cm/°C | |
| Transverse 2 | 3.5E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.30 | W/m/K | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 13 | kV/mm | ASTM D149 |
| Arc Resistance | 188 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 150 | °C | |
| Injection Pressure | 3.50 to 6.50 | MPa |
| Note Message | |
|---|---|
| 1 . | XY Direction |
| 2 . | Z Direction |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durethan® BG 30 X H2.0 XF 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| MAJORIS FN020 - NATFL | AD majoris | PP Homopolymer | MAJORIS |
| OP - PSU 30GF | Oxford Polymers | PSU | OP - PSU |
| Petrothene® NA217000 | LyondellBasell Industries | LDPE | Petrothene® |
| Daelim Po1y® XP9200N | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |