Stanyl® HFX50S
| Category: | Nylon, Unspecified , Polyamide |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Stanyl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hWOa4x_StanylHFX50S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Stanyl®HFX50S is a polyamide material, which contains a 30% glass fiber reinforced material. This product is available in the Asia-Pacific region,. Stanyl®The main features of HFX50S are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.46 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.2 | -- | % | ISO 294-4 |
| Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.7 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11500 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.9 | -- | % | ISO 527-2 |
| Flexural Modulus | 11000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 7.0 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 285 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 305 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Strength | 30 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 4.30 | 5.20 | IEC 60250 | |
| 1 MHz | 3.90 | 4.20 | IEC 60250 | |
| 1.00 GHz | 3.70 | 3.90 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.40 mm) | V-0 | -- | IEC 60695-11-10, -20 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Rear Temperature | 300 - 310 | °C | |
| Middle Temperature | 305 - 315 | °C | |
| Front Temperature | 310 - 320 | °C | |
| Nozzle Temperature | 315 - 325 | °C | |
| Processing (Melt) Temp | 320 - 330 | °C | |
| Mold Temperature | 100 - 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.500 - 3.00 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COPYLENE® CH085S | Phillips 66 | PP Homopolymer | COPYLENE® |
| LNP™ THERMOCOMP™ Noryl_FM3020 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ THERMOCOMP™ |
| MAGNUM™ 3904 Smooth | Trinseo | ABS | MAGNUM™ |
| PERLEX® R271 | A. Schulman Europe | PC | PERLEX® |
| Polene EVA SV1055 | TPI Polene Public Company Limited | EVA | Polene EVA |