MonoSol® AF A200
| Category: | PVOH , Polyvinyl Alcohol |
| Manufacturer: | MonoSol, LLC |
| Trademark: | MonoSol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hWFRgW_MonoSol-AF-A200.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MonoSol AF A200 is a PVOH based thermoplastic film, soluble in hot water and manufactured using MonoSol AF's proprietary blown film technology. MonoSol AF A200 is a typical grade of PVOH hot water-soluble film. It is soluble above 60°C with agitation. It has limited cold wet strength and is primarily used for hospital laundry bags where the bulk of the linen is dry. It can also be used on some VFFS packaging machinery for chemical portion packaging applications where the pack is being put into an environment with water above 60°C with agitation. Available thickness range is 20 micron (0.8 mil) to 80 micron (3.1 mil). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Moisture Content (23°C) 1 | 6.7 | wt% | |
| Solubility 2 | |||
| Disintegration : 60°C, 20.0 µm | 1.0 | sec | |
| Disintegration : 70°C, 20.0 µm | 1.0 | sec | |
| Dissolution : 60°C, 20.0 µm | 430.0 | sec | |
| Dissolution : 70°C, 20.0 µm | 300.0 | sec |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Yield (20.0 µm) | 40.1 | m²/kg | ASTM D4321 |
| Film Thickness - Tested | 20 | µm | |
| Film Thickness - Recommended / Available | 20 µm to 80 µm | ||
| Secant Modulus | ASTM D882, ISO 527-3 | ||
| 10%, MD : 20 µm | 238 | MPa | |
| 100%, MD : 20 µm | 64.8 | MPa | |
| 10%, TD : 20 µm | 290 | MPa | |
| 100%, TD : 20 µm | 45.5 | MPa | |
| Tensile Strength | |||
| MD : Break, 20 µm | 71.7 | MPa | ASTM D882 |
| TD : Break, 20 µm | 77.9 | MPa | ASTM D882 |
| MD : 20 µm | 71.7 | MPa | ISO 527-3 |
| TD : 20 µm | 77.9 | MPa | ISO 527-3 |
| Tensile Elongation | ASTM D882, ISO 527-3 | ||
| MD : Break, 20 µm | 130 | % | |
| TD : Break, 20 µm | 230 | % | |
| Dart Drop Impact (20 µm) | 290 | g | ASTM D1709, DIN 53433 |
| Elmendorf Tear Strength | |||
| MD : 20 µm | 300 | g | ASTM D1922 |
| TD : 20 µm | 300 | g | ASTM D1922 |
| MD : 20 µm | 0.031 | N | ISO 6383-2 |
| TD : 20 µm | 0.031 | N | ISO 6383-2 |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | Distilled Water (MSTM 205) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 69 GF 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| Cellophane™ 400P23 | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Celstran® PP-GF40-0455 P10/10 | Celanese Corporation | PP, Unspecified | Celstran® |
| Dow ENDURANCE™ HFDA-0693 BK LS | The Dow Chemical Company | TP, Unspecified | Dow ENDURANCE™ |
| ISOPAK® 525 Black | Great Eastern Resins Industrial Co., Ltd. (GRECO) | ABS | ISOPAK® |