LOTADER® 3210 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.

Applications
LOTADER® 3210 is a versatile adhesive for extrusion coating or lamination, designed as :

Concentrate to be used in dry blend with LDPE. LOTADER® 3210 improves adhesion of LDPE on aluminium foils, metallized or primerized films.

Ready for use resin to be used pure. LOTADER® 3210 gives excellent adhesion on substrates likes aluminium foil, metallized plastics, paper, board, PE and some plastic films like BOPP.

Coextrusion tie layer for PE/PA in extrusion coating process.

LOTADER® 3210 is also a coupling agent for mineral filled compounds such as halogen free flame retardant wires and cables, a compatibilizer for polyamide/polyolefin blends and a modifier for polyamides.

General Information
Features	Good Adhesion High Melt Stability Terpolymer
Uses	Adhesives Bi-axially Oriented Film Coating Applications Compounding Laminates
Forms	Pellets
Processing Method	Coextrusion Compounding Extrusion Extrusion Coating Laminating

Physical	Nominal Value	Unit	Test Method
Density	0.940	g/cm³	ISO 1183, ASTM D1505
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	5.0	g/10 min	ASTM D1238, ISO 1133
n-Butyl Acrylate Content	6.0	wt%
Maleic Anhydride Content	3.1	wt%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	46		ASTM D2240, ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Break, Compression Molded)	12.0	MPa	ASTM D638, ISO 527-2
Tensile Elongation (Break, Compression Molded)	600	%	ASTM D638, ISO 527-2
Flexural Modulus (Compression Molded)	120	MPa	ASTM D790, ISO 178

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	76.0	°C	ISO 306/A, ASTM D1525 ¹
Melting Temperature	107	°C	ISO 11357-3

Note Message
1 .	Loading 1 (10 N)

Resin Grade	Manufacturer	Category	Trademark
Mirakutoran® TPU E890PBOO	Japan Mirakutoran Inc.	TPU Alloy	Mirakutoran® TPU
Shinko-Lac® ABS TR-2	Mitsubishi Rayon America Inc.	ABS	Shinko-Lac®
StarCLEAR CLR-1045	STAR Thermoplastic Alloys & Rubbers, Inc.	TPE	StarCLEAR
Hylon® N1220HL	Ravago Manufacturing Americas, LLC	Nylon 66	Hylon®
apilon 52® DP1805	API SpA	TPU-Polyester	apilon 52®