TAISOX 9003
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Formosa Plastics Corporation |
| Trademark: | TAISOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hVadYX_TAISOX-9003.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAISOX 9003 is a high density polyethylene material,. This product is available in North America, Europe or Asia Pacific region. The processing method is blow molding. The main features of TAISOX 9003 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.25 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | 200 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 66 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 27.9 | MPa | ASTM D638 |
| Fracture | 34.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1000 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 392 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 124 | °C | ASTM D1525 |
| Melting Temperature | 132 | °C |
| Additional Information |
|---|
| Notched Izod Impact Strength, ASTM D256: 13 kg-cm/cm²Die Swell Ratio, FPC Method: 1.52Pich-off thickness, FPC Method: Good |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 160 - 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Synprene™ RT-5190 RoHS Black | PolyOne Corporation | SBC | Synprene™ |
| apilon 52c® C MG 100A | API SpA | TPU-Polyether | apilon 52c® |
| Clariant Nylon 6 PA223 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| LUVOCOM® 1-7532 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Pebax® Rnew 25R53 SP 01 | Arkema | PEBA-Ether | Pebax® Rnew |